ASTM A358/A358M-19
Standard Specification for Electric-Fusion-Welded Austenitic Chromium-Nickel Stainless Steel Pipe for High-Temperature Service and General Applications
Translate name
STANDARD published on 1.11.2019
The information about the standard:
Designation standards: ASTM A358/A358M-19
Note: WITHDRAWN
Publication date standards: 1.11.2019
SKU: NS-976066
The number of pages: 8
Approximate weight : 24 g (0.05 lbs)
Country: American technical standard
Category: Technical standards ASTM
The category - similar standards:
Annotation of standard text ASTM A358/A358M-19 :
Keywords:
arc welded steel pipe, austenitic stainless steel, chromium-nickel steel, fusion welded steel pipe, high temperature application, steel pipe, temperature service applications, high, welded steel pipe ,, ICS Number Code 23.040.10 (Iron and steel pipes)
Additional information
| 1. Scope | ||||||||||||
|
1.1 This specification2 covers electric-fusion-welded austenitic chromium-nickel stainless steel pipe suitable for corrosive or high-temperature service, or both, or for general applications. Note 1: The dimensionless designator NPS (nominal pipe size)
has been substituted in this standard for such traditional terms as
“nominal diameter,” “size,” and “nominal size.”
1.2 This specification covers the grades of alloy and stainless steel listed in Table 1. The selection of the proper grade and requirements for heat treatment shall be at the discretion of the purchaser, dependent on the service conditions to be encountered. 1.3 Five classes of pipe are covered as follows: 1.3.1 Class 1—Pipe shall be double welded by processes employing filler metal in all passes and shall be completely radiographed. 1.3.2 Class 2—Pipe shall be double welded by processes employing filler metal in all passes. No radiography is required. 1.3.3 Class 3—Pipe shall be single welded by processes employing filler metal in all passes and shall be completely radiographed. 1.3.4 Class 4—Same as Class 3 except that the weld pass exposed to the inside pipe surface may be made without the addition of filler metal (see 6.2.2.1 and 6.2.2.2). 1.3.5 Class 5—Pipe shall be double welded by processes employing filler metal in all passes and shall be spot radiographed. 1.4 Supplementary requirements covering provisions ranging from additional testing to formalized procedures for manufacturing practice are provided. Supplementary Requirements S1 through S6 are included as options to be specified when desired. 1.5 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the specification. The inch-pound units shall apply unless the “M” designation of this specification is specified in the order. 1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee. |
||||||||||||
| 2. Referenced Documents | ||||||||||||
|
We recommend:
Technical standards updating
Do you want to make sure you use only the valid technical standards?
We can offer you a solution which will provide you a monthly overview concerning the updating of standards which you use.
Would you like to know more? Look at this page.