ASTM A565/A565M-10(2017)e1
Standard Specification for Martensitic Stainless Steel Bars for High-Temperature Service (Includes all amendments and changes 3/17/2017).
Translate name
STANDARD published on 15.3.2017
The information about the standard:
Designation standards: ASTM A565/A565M-10(2017)e1
Publication date standards: 15.3.2017
SKU: NS-677549
The number of pages: 4
Approximate weight : 12 g (0.03 lbs)
Country: American technical standard
Category: Technical standards ASTM
The category - similar standards:
Annotation of standard text ASTM A565/A565M-10(2017)e1 :
This guide covers standard specification for hot-finished and cold-finished martensitic chromium steel bars for high-temperature service. The mechanical properties shall be developed by suitable heat treatment, as indicated for each alloy. The steel shall conform to the required chemical composition for carbon, manganese, phosphorus, sulfur, silicon, chromium, nickel, molybdenum, vanadium, tungsten, nitrogen, aluminum, columbium, and copper. The microstructure shall not contain more than 5% delta-ferrite after full heat treatment. The material shall conform to the required mechanical properties such as tensile strength, yield strength, elongation, impact strength, and Brinell hardness. The material shall also undergo stress rupture testing using a combination test bar.
Keywords:
martensitic stainless steel, stainless steel bars, stainless steel billets, stainless steel forgings, temperature service applications´high,, ICS Number Code 77.140.60 (Steel bars and rods), 77.140.85 (Iron and steel forgings)
Additional information
| 1. Scope | ||||||||||||||||||
|
1.1 This specification covers hot-finished and cold-finished martensitic chromium steel bars for high-temperature service. The mechanical properties are developed by suitable heat treatment, as indicated for each alloy. 1.2 Where strength at temperature is a factor, these steels are generally limited to a maximum service temperature of 1200°F [650°C]. For oxidation (scaling) resistance and at low stresses, these steels are useful to 1450°F [790°C]. 1.3 This specification is expressed in both inch-pound units and SI units; however, unless the purchase order or contract specifies the applicable M specification designation (SI units), the inch-pound units shall apply. The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the specification. |
||||||||||||||||||
| 2. Referenced Documents | ||||||||||||||||||
|
We recommend:
Updating of laws
Do you want to be sure about the validity of used regulations?
We offer you a solution so that you could use valid and updated legislative regulations.
Would you like to get more information? Look at this page.