ASTM A814/A814M-15e1
Standard Specification for Cold-Worked Welded Austenitic Stainless Steel Pipe (Includes all amendments And changes 3/12/2019).
Automatically translated name:
Standard Specification for Cold-Worked Welded Austenitic Stainless Steel Pipe
STANDARD published on 1.3.2015
The information about the standard:
Designation standards: ASTM A814/A814M-15e1
Note: WITHDRAWN
Publication date standards: 1.3.2015
SKU: NS-586939
The number of pages: 7
Approximate weight : 21 g (0.05 lbs)
Country: American technical standard
Category: Technical standards ASTM
The category - similar standards:
Annotation of standard text ASTM A814/A814M-15e1 :
Keywords:
austenitic stainless steel pipe, cold-worked pipe,, ICS Number Code 23.040.10 (Iron and steel pipes)
Additional information
| 1. Scope | ||||||||||||||||||||
|
1.1 This specification covers two classes of flanged and cold-bending quality cold-worked straight-seam single or double welded austenitic steel pipe intended for high-temperature and general corrosive services. Note 1: When the impact test criterion for a low-temperature
service would be 15 ft·lbf [20 J] energy absorption or 15 mils
[0.38 mm] lateral expansion, some of the austenitic stainless steel
grades covered by this specification are accepted by certain
pressure vessel or piping codes without the necessity of making the
actual test. For example, Grades 304, 304L, and 347 are accepted by
the ASME Pressure Vessel Code, Section VIII Division 1, and by the
Chemical Plant and Refinery Piping Code, ANSI B31.3 for service at
temperatures as low as −425 °F [−250 °C] without qualification by
impact tests. Other AISI stainless steel grades are usually
accepted for service temperatures as low as −325 °F [−200 °C]
without impact testing. Impact testing may, under certain
circumstances, be required. For example, materials with chromium or
nickel content outside the AISI ranges, and for material with
carbon content exceeding 0.10 %, are required to be impact tested
under the rules of ASME Section VIII Division 1 when service
temperatures are lower than −50 °F [−45 °C].
1.2 Grades TP304H, TP304N, TP316H, TP316N, TP321H, TP347H, and TP348H are modifications of Grades TP304, TP316, TP321, TP347, and TP348, and are intended for high-temperature service. 1.3 Two classes of pipe are covered as follows: 1.3.1 Class SW—Pipe, single-welded with no addition of filler metal and 1.3.2 Class DW—Pipe, double-welded with no addition of filler metal. 1.4 Optional supplementary requirements are provided for pipe where a greater degree of testing is desired. These supplementary requirements call for additional tests to be made and, when desired, one or more of these may be specified in the order. 1.5 Table 1 lists the dimensions of cold-worked single- or double-welded stainless steel pipe. Pipe having other dimensions may be furnished provided such pipe complies with all other requirements of this specification. 1.6 The values stated in either
inch-pound units or SI units are to be regarded separately as
standard. Within the text, the SI units are shown in brackets. The
values stated in each system are not exact equivalents; therefore,
each system must be used independently of the other. Combining
values from the two systems may result in nonconformance with the
specification. The inch-pound units shall apply unless the “M”
designation of this specification is specified in the order.
|
||||||||||||||||||||
| 2. Referenced Documents | ||||||||||||||||||||
|
Similar standards:
Historical
1.5.2014
Historical
1.12.2010
Historical
1.5.2013
Historical
1.5.2014
Historical
1.3.2014
Historical
1.3.2014
We recommend:
Technical standards updating
Do you want to make sure you use only the valid technical standards?
We can offer you a solution which will provide you a monthly overview concerning the updating of standards which you use.
Would you like to know more? Look at this page.