ASTM E2627-13

5.1 This practice provides a way to estimate the average grain size of polycrystalline materials. It is based on EBSD measurements of crystallographic orientation which are inherently quantitative in nature. This method has specific advantage over traditional optical grain size measurements in some materials, where it is difficult to find appropriate metallographic preparation procedures to adequately delineate grain boundaries.

1.1 This practice is used to determine grain size from measurements of grain areas from automated electron backscatter diffraction (EBSD) scans of polycrystalline materials.

1.2 The intent of this practice is to standardize operation of an automated EBSD instrument to measure ASTM 1.3 This practice is only applicable to fully recrystallized materials.

1.4 This practice is applicable to any crystalline material which produces EBSD patterns of sufficient quality that a high percentage of the patterns can be reliably indexed using automated indexing software.

1.5 The practice is applicable to any type of grain structure or grain size distribution.

1.6 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.

1.7 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.